Evaluation of penetration depth and color stability of experimental infiltrants on surface lesion in human enamel
DOI:
https://doi.org/10.34117/bjdv11n2-052Keywords:
demineralization tooth, dental caries, composite resins, pigmentationAbstract
Background: This study evaluated the chemical properties of different experimental infiltrants. Materials and Methods: The blocks were submitted to simulation of superficial lesion in demineralizing solution (pH=4.5). The specimens were divided into groups for infiltrants application: IC (Icon®), E (Experimental); ED (Experimental + 0.5% DFI), EH (Experimental + 10% HEMA), EHD (Experimental + 10% HEMA + 0.5% DFI); EEt (Experimental + 10% Ethanol) e EEtD (Experimental + 10% Ethanol + 0.5% DFI). The specimens infiltrated were submitted to penetration depth (PD) and color stability (CS). For the evaluation of degree conversion (DC) the specimens of infiltrants materials were prepared. Data were analyzed by generalized linear models (p=0.05). Results: For CS, all pigmented groups when submitted to coffee and red wine, however in coffee there was no statistical difference, and the IC, when pigmented with red wine, showed the greatest color change (p <0.05). Additionally, the IC group had the lowest DC, differing statistically from the other groups (p<0.05). Conclusion: The experimental infiltrants showed characteristics similar to the commercial infiltrant Icon®, and the association in its composition of Ethanol with DFI improved the degree of conversion of the material. Clinical significance: Low viscosity resins, also called infiltrants, may be a viable alternative to masking surface and white spot lesions as they may pigment less than other direct restorative materials.
References
[ 1 ] Ceci M, Rattalino D, Viola M, Beltrami R, Chiesa M, Colombo M, Poggio C. Resin infiltrant for non-cavitated caries lesions: evaluation of color stability. J Clin Exp Dent. 2017. 1; 9(2): 231-7.
[ 2 ] Meyer-Lueckel H e Paris S. Progression of artificial enamel caries lesions after infiltration with experimental light curing resins. Caries Res. 2008a;42(2):117–24.
[ 3 ] Park J, Eslick J, Ye Q, Misra A and Spencer P. The influence of chemical structure on the properties in methacrylate-based dentin adhesives. Dent Mater. 2011; 27: 1086-93.
[ 4 ] Meyer-Lueckel H, Paris S, Kielbassa AM. Surface layer erosion of natural caries lesions with phosphoric and hydrochloric acid gels in preparation for resin infiltration. Caries Res. 2007;41(3):223–30.
[ 5 ] Meyer-Lueckel H e Paris S. Improved resin infiltration of natural caries lesions. J Dent Res. 2008b; 87(12):1112–7.
[ 6 ] Paris S, Meyer-Lueckel H and Kielbassa AM. Resin infiltration of natural caries lesions. J Dent Res. 2007a; 86(7):662-6.
[ 7 ] Paris S, Meyer-Lueckel H, Colfen H, Kielbassa A. Resin infiltration of artificial enamel caries lesions with experimental light curing resins. Dent Mater J. 2007b; 26:582-588.
[ 8 ] Silva SN, Reich AM, DeLeon E Jr, Schafer T, Rueggeberg FA, Fortson WM Jr. Staining potential differences between an infiltrative resin and an esthetic, flowable composite. J Esthet Restor Dent. 2018 30(5): 457-463.
[ 9 ] Paris S and Meyer-Lueckel H. Masking of labial enamel white spot lesions by resin infiltration: a clinical report. Quintessence Int. 2009; 40:713–8.
[ 10 ] Araújo GSA, Sfalcin RA, Araújo TGF, Alonso RCB, Puppin-Rontani RG. Evaluation of polymerization characteristics and penetration into enamel caries lesion of experimental infiltrants. J Dent. 2013; 21:1014-9.
[ 11 ] Araujo TGF, Sfalcin A, Spagnolo G, Araújo A De, Brusch C, Puppin-rontani RM. Bond strength of experimental low-viscosity resin materials to early enamel caries lesions: effect of diluent / solvent addition. J Adhes Dent. 2015a;17(2):117–23.
[ 12 ] Meyer-Lueckel H, Paris S. Infiltration of natural caries lesions with experimental resins differing in penetration coefficients and ethanol addition. Caries Res. 2010;44(4):408–14.
[ 13 ] Paris S, Schwentke F, Seddig S, Müller WD, Dörfer C, Meyer-Lueckel H. Micro-hardness and mineral loss of enamel lesions after infiltration with various resins: Influence of infiltrant composition and application frequency in vitro. J Dent. 2013; 41:543–48.
[ 14 ] Gelani R, Zandona AF, Lippert F, Kamocka MM, Eckert G. In vitro progression of artificial white spot lesions sealed with an infiltrant resin. Operat Dent. 2014; 39-5: 481-8.
[ 15 ] Gölz L, Simonis RA, Reichelt J, Stark H, Frentzen M, Allam J-P, Probstmeier R, Winter J, Kraus D. In vitro biocompatibility of ICON® and TEGDMA on human dental pulp stem cells. Dent Mater. 2016; 32: 1052-64.
[ 16 ] Paris S and Meyer-Lueckel H. Inhibition of caries progression by resin infiltration in situ. Caries Res. 2010; 44:47–54.
[ 17 ] Al-Samadani KH J. Color stability of restorative materials in response to Arabic coffee, Turkish coffee and nescafe. Contemp Dent Pract. 2013; 14: 681-90.
[ 18 ] Anfe TE, Agra CM, Vieira GF. Evaluation of the possibility of removing staining by repolishing composite resins submitted to artificial aging. J Esthet Restor Dent. 2011; 23: 260-7.
Awliya WY, Al-Alwani DJ, Gashmer ES, Al-Mandil HB. The effect of commonly used types of coffee on surface microhardness and color stability of resin-based composite restorations. Saud Dent J. 2010; 22: 177-81.
[ 20 ] Gönülol N, Yilmaz F. The effects of finishing and polishing techniques on surface roughness and color stability of nanocomposites. J Dent 2012;40 (2):64-70.
[ 21 ] Kerby RE, Knobloch LA, Schricker S, Gregg B. Synthesis and evaluation of modified urethane dimethacrylate resins with reduced water sorption and solubility. Dent Mater. 2009; 25:302–13.
[ 22 ] Kim TH, García-Godoy F, Ko CC, Park JK, Kim HI, Kwon YH. Effect of temperature on the mass and color stability of additional photoinitiator containing composite resins. Dent Mater J 2013;32(4):628-36.
[ 23 ] Martino S, Tellez M, Santamaría RM, Gomez J, Ekstrand KR. Sealing distal proximal caries lesions in first primary molars: efficacy after 2.5 years. Caries Res. 2010; 44: 562-70.
[ 24 ] Gonçalves F, Kawano Y, Pfeifer C, Stansbury JW, Braga RR. Influence of BisGMA, TEGDMA, and BisEMA contents on viscosity, conversion, and flexural strength of experimental resins and composites. Eur J Oral Sci. 2009;117(4):442-6.
[ 25 ] Schwendicke F, Paris S, Stolpe M. Detection and treatment of proximal caries lesions: Milieu-specific cost-effectiveness analysis. J Dent. Elsevier Ltd; 2015;43(6):647–55.
[ 26 ] Paris S, Sevier VM, Chatzidakis AJ, Meyer-Lueckel H. Penetration of experimental infiltrants with different penetration coefficients and ethanol addition into natural caries lesions in primary molars. Caries Res. 2012b;46(2):113-7.
[ 27 ] JK, Kim TH, Ko CC, Garcia-Godoy F, Kim HI, & Kwon YH. Effect of staining solutions on discoloration of resin nanocomposites. American J Dent. 2010. 23(1): 39-42.
[ 28 ] Peris A R, Mitsui F H O, Lobo M, Bedran-russo A K B, Marchi G M. Adhesive systems and secondary caries formation: Assessment of dentin bond strength, caries lesions depth and fluoride release. Dent Mater. 2007; 23: 308-16.
[ 29 ] Andrade KM, Palialol AR, Lancellotti AC, Aguiar FH, Watts DC, Gonçalves LS, et al. Effect of diphenyliodonium hexafluorphosphate on resin cements containing different concentrations of ethyl 4- dimethylamino) benzoate and 2-(dimethylamino)ethylmethacrylate as co-initiators. Dent Mater. 2016 Jun;32(6):749-55.
[ 30 ] Dressano D, Palialol AR, Xavier TA, Braga RR, Oxman JD, Watts DC, Marchi GM, Lima AF. Effect of diphenyliodonium hexafluorophosphate on the physical and chemical properties of ethanolic solvated resins containing camphorquinone and 1-phenyl-1,2-propanedione sensitizers as initiators. Dent Mater. 2016 Jun;32(6):756-64.
[ 31 ] Gonçalves LS, Moraes RR, Ogliari FA, Boaro L, Braga RR, Consani S. Improved polymerization efficiency of methacrylate-based cements containing an iodonium salt. Dent Mater. 2013 Dec;29(12):1251-5.
[ 32 ] Mathias C, Gomes RS, Dressano D, Braga, RR, Aguiar, FHB, Marchi, GM. Effect of diphenyliodonium hexafluorophosphate salt on experimental infiltrants containing different diluents. Odontol. 2018 Oct.
[ 33 ] Ogliari FA, Ely C, Petzhold CL, Demarco FF, Piva E. Onium salt improves the polymerization kinetics in an experimental dental adhesive resin. J Dent. 2007;35(7):583–7.
[ 34 ] Ogliari A, Ely C, Lima GS, Conde MCM, Petzhold CL. Onium salt reduces the inhibitory polymerization effect from an organic solvent in a model dental adhesive resin. J Biomed Mater Res Part B Appl. 2008;86: 113–8.
[ 35 ] Wefel JS, Heilman JR, Jordan TH. Comparisons of in vitro root caries models. Caries Res 1995; 29: 2004-209.
[ 36 ] Borges A, Caneppele T, Luz M, Pucci C, Torres C. Color stability of resin used for caries infiltration after exposure to different staining solutions. Oper Dent. 2014; 39:433-440
[ 37 ] Araújo GSA, Naufel FS, Alonso RCB, Lima DANL, and Puppin-Rontani RM. Influence of staining solution and bleaching on color stability of resin used for caries infiltration. Oper Dent. 2015b,40(6): E250-E256.
[ 38 ] Thumu J, Kadiyala A, Bollu IP, Ballullaya SV, Devalla S. Effect of staining solutions on the color stability of conventional and bulk fill nanohybrid resin composites: a spectrophotometric analysis. J Oper Dent Endodon. 2017; 2(1):1-5.
[ 39 ] Rey N, Benbachirc, Bortolotto T and Krejci I. Evaluation of the staining potential of a caries infiltrant in comparison to other products. Dental Mater J 2014; 33(1): 86–91
[ 40 ] Leland A, Akyalcin S, English JD, Tufekci E, Paravina R. Evaluation of staining and color changes of a resin infiltration system. Angle Orthod. 2016; 86:900-904.
[ 41 ] Borges A, Caneppele T, Masterson D, Maia L. Is resin infiltration an effective esthetic treatment for enamel development defects and white spot lesions? A systematic review. J Dent. 2017; 56:11-18
[ 42 ] Collares FM, Ogliari FA, Zanchi CH, Petzhold CL, Piva E, Samuel SM. Influence of 2-hydroxyethyl methacrylate concentration on polymer network of adhesive resin. J Adhes Dent. 2011 Apr;13(2):125-9.
[ 43 ] Van Landuyt KL, Snauwaert J, De Munck J, Peumans M, Yoshida Y, Poitevin A, Coutinho E, Suzuki K, Lambrechts P, Van Meerbeek B. Systematic review of the chemical composition of contemporary dental adhesives. Biomaterials. 2007 Sep;28(26):3757-85.